STUDI PELAPISAN HIDROKSIAPATIT PADA STAINLESS STEEL 316L UNTUK APLIKASI COATING DENTAL IMPLANT |
|
BACA FULL TEXT ABSTRAK Permintaan Versi cetak |
|
Pengarang | Ireka Salsabila - Personal Name |
---|---|
Subject | FLUORIDATION-DENTAL DISEASE PREVENTION |
Bahasa | Indonesia |
Fakultas | FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SYIAH KUALA |
Tahun Terbit | 2018 |
Abstrak/Catatan ABSTRAK Telah dilakukan penelitian yang mengkaji pengaruh variasi temperatur sintering dan variasi komposisi air dalam suspensi terhadap karakteristik lapisan hidroksiapatit (ukuran kristal, derajat kristalinitas, dan ketebalan) berbasis tulang sapi untuk aplikasi coating dental implant. Hidroksiapatit disintesis dari tulang sapi yang dikalsinasi terlebih dahulu pada temperatur 1000ºC selama 6 jam untuk dimanfaatkan kandungan kalsium oksidanya (CaO). Kemudian, serbuk CaO direaksikan dengan asam posfat (H3PO4) dan selanjutnya disintering pada temperatur 900ºC selama 2 jam. Penentuan fasa CaO dan hidroksiapatit ini dilakukan dengan melakukan pengujian XRD (X-Ray Diffraction). Hidroksiapatit yang telah berhasil disintesis ini kemudian di coating pada plat Stainless Steel 316L menggunakan metode Dip-Coating dengan variasi komposisi air dalam suspensi hidroksiapatit masing-masing 4 gram, 6 gram, 8 gram, dan 10 gram. Setelah hidroksiapatit berhasil di coating, untuk selanjutnya lapisan hidroksiapatit dapat diaplikasikan sebagai material coating dental implant dengan variasi temperatur sintering masing-masing 500ºC, 600ºC, 700ºC, dan 800ºC selama 1 jam. Berdasarkan hasil pengujian XRD, fasa CaO dan hidroksiapatit telah berhasil terbentuk. Hasil karakterisasi menunjukkan bahwa proses sintering dan penambahan komposisi air dalam suspensi mempengaruhi nilai ukuran kristal dan ketebalan yang dihasilkan: ukuran kristal yaitu 20.10 nm – 46.94 nm, ketebalan yaitu 260 μm – 780 μm (>25 μm), dengan nilai derajat kristalinitas yang dihasilkan adalah ≈100% (>45%). Merujuk nilai ukuran kristal dan derajat kristalinitas yang dihasilkan, maka material hidroksiapatit ini telah memenuhi karakteristik material coating dental implant. Namun jika merujuk nilai ketebalan lapisan yang dihasilkan, masih belum memenuhi karakteristik untuk aplikasi material coating dental implant. Kata kunci: Tulang sapi murni, hidroksiapatit, dip coating, stainless steel 316L, material coating dental implant, ukuran kristal, derajat kristalinitas, ketebalan. ABSTRACT The effect of sintering temperature variation and water compositions into suspense variation to the characteristic of hydroxyapatite coating (crystallite size, degree of crystallinity, and thickness) of bovine bone for coating dental implant application has been done. In this research, hydroxyapatite was synthesized from bovine bone that calcined first at 1000ºC temperature for 6 hours to be used the content of its calcium oxide (CaO). Then, CaO substance was reacted with phosphate acid (H3PO4) and then sintering at 900ºC for 2 hours. The determination of this CaO phase and hydroxyapatite was done with XRD (X-Ray Diffraction) testing. The hydroxyapatite that has been successfully synthesized then coated at Stainless Steel 316L using Dip-Coating method with water compositions into suspense variation each 4 gram, 6 gram, 8 gram, and 10 gram. After the hydroxyapatite that has been successful coated,to be applied as coating dental implant with sintering temperature variation each 500ºC, 600ºC, 700ºC, and 800ºC for 1 hours. From the pattern of XRD test, CaO phase and hydroxyapatite has been successful formed. Based on characterization result shown that sintering process and water compositions addition into suspense has effected the result of crystallite size and thickness with the result of crystallite size was 20.10 nm – 46.94 nm, thickness was 260 μm – 780 μm (>25 μm), with the result for degree of crystallinity was ≈100% (>45%). Based on the result of crystallite size and degree of crystallinity, this hydroxyapatite material has been conform the characteristic of coating dental implant material. But, based on the result of coating thickness, it still does not conform characteristic of coating dental implant material. Keywords: The pure bovine bone, hydroxyapatite, dip coating, stainless steel 316L, coating dental implant material, crystallite size, degree of crystallinity, thickness. | |
Tempat Terbit | Banda Aceh |
Literature Searching Service | Hard copy atau foto copy dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan isi formulir online (Chat Service LSS) |
Share Social Media | |
Tulisan yang Relevan PENGARUH VARIASI WAKTU TAHAN SINTERING TERHADAP KARAKTERISTIK COATING DENTAL IMPLANT BERBASIS HAP DARI TULANG SAPI (MAISARAH, 2015) |
|
Kembali ke sebelumnya |