Ireka Salsabila. STUDI PELAPISAN HIDROKSIAPATIT PADA STAINLESS STEEL 316L UNTUK APLIKASI COATING DENTAL IMPLANT. Banda Aceh : Universitas Syiah Kuala, 2018 |
|
AbstrakAbstrak
telah dilakukan penelitian yang mengkaji pengaruh variasi temperatur sintering dan variasi komposisi air dalam suspensi terhadap karakteristik lapisan hidroksiapatit (ukuran kristal, derajat kristalinitas, dan ketebalan) berbasis tulang sapi untuk aplikasi coating dental implant. hidroksiapatit disintesis dari tulang sapi yang dikalsinasi terlebih dahulu pada temperatur 1000ºc selama 6 jam untuk dimanfaatkan kandungan kalsium oksidanya (cao). kemudian, serbuk cao direaksikan dengan asam posfat (h3po4) dan selanjutnya disintering pada temperatur 900ºc selama 2 jam. penentuan fasa cao dan hidroksiapatit ini dilakukan dengan melakukan pengujian xrd (x-ray diffraction). hidroksiapatit yang telah berhasil disintesis ini kemudian di coating pada plat stainless steel 316l menggunakan metode dip-coating dengan variasi komposisi air dalam suspensi hidroksiapatit masing-masing 4 gram, 6 gram, 8 gram, dan 10 gram. setelah hidroksiapatit berhasil di coating, untuk selanjutnya lapisan
Baca Juga : PENGARUH VARIASI WAKTU TAHAN SINTERING TERHADAP KARAKTERISTIK COATING DENTAL IMPLANT BERBASIS HAP DARI TULANG SAPI (MAISARAH, 2015) ,
Baca Juga : PENGARUH VARIASI TEMPERATUR SINTERING TERHADAP KARAKTERISTIK HIDROKSIAPATIT (HAP) BERBASIS TULANG SAPI UNTUK APLIKASI COATING DENTAL IMPLANT (Nurul Fadhilah, 2016) , oksiapatit dapat diaplikasikan sebagai material coating dental implant dengan variasi temperatur sintering masing-masing 500ºc, 600ºc, 700ºc, dan 800ºc selama 1 jam. berdasarkan hasil pengujian xrd, fasa cao dan hidroksiapatit telah berhasil terbentuk. hasil karakterisasi menunjukkan bahwa proses sintering dan penambahan komposisi air dalam suspensi mempengaruhi nilai ukuran kristal dan ketebalan yang dihasilkan: ukuran kristal yaitu 20.10 nm – 46.94 nm, ketebalan yaitu 260 ?m – 780 ?m (>25 ?m), dengan nilai derajat kristalinitas yang dihasilkan adalah ?100% (>45%). merujuk nilai ukuran kristal dan derajat kristalinitas yang dihasilkan, maka material hidroksiapatit ini telah memenuhi karakteristik material coating dental implant. namun jika merujuk nilai ketebalan lapisan yang dihasilkan, masih belum memenuhi karakteristik untuk aplikasi material coating dental implant. kata kunci: tulang sapi murni, hidroksiapatit, dip coating, stainless steel 316l, material coating dental implant, ukuran kristal, derajat kristalinitas, ketebalan. abstract the effect of sintering temperature variation and water compositions into suspense variation to the characteristic of hydroxyapatite coating (crystallite size, degree of crystallinity, and thickness) of bovine bone for coating dental implant application has been done. in this research, hydroxyapatite was synthesized from bovine bone that calcined first at 1000ºc temperature for 6 hours to be used the content of its calcium oxide (cao). then, cao substance was reacted with phosphate acid (h3po4) and then sintering at 900ºc for 2 hours. the determination of this cao phase and hydroxyapatite was done with xrd (x-ray diffraction) testing. the hydroxyapatite that has been successfully synthesized then coated at stainless steel 316l using dip-coating method with water compositions into suspense variation each 4 gram, 6 gram, 8 gram, and 10 gram. after the hydroxyapatite that has been successful coated,to be applied as coating dental implant with sintering temperature variation each 500ºc, 600ºc, 700ºc, and 800ºc for 1 hours. from the pattern of xrd test, cao phase and hydroxyapatite has been successful formed. based on characterization result shown that sintering process and water compositions addition into suspense has effected the result of crystallite size and thickness with the result of crystallite size was 20.10 nm – 46.94 nm, thickness was 260 ?m – 780 ?m (>25 ?m), with the result for degree of crystallinity was ?100% (>45%). based on the result of crystallite size and degree of crystallinity, this hydroxyapatite material has been conform the characteristic of coating dental implant material. but, based on the result of coating thickness, it still does not conform characteristic of coating dental implant material. keywords: the pure bovine bone, hydroxyapatite, dip coating, stainless steel 316l, coating dental implant material, crystallite size, degree of crystallinity, Pengarang tidak dapat memberikan Full Text secara langsung, untuk mendapatkan full text silahkan menghubungi email pengarang : salsabila.ireka@gmail.com atau dapat mengisi Form LSS di bawah. Literature Searching ServiceTulisan yang relevan HISTOPATOLOGI GINJAL TIKUS PUTIH (RATTUS NORVEGICUS) SETELAH IMPLAN WIRE MATERIAL LOGAM (Tridian Novia Gelis, 2020) ,GAMBARAN KECEMASAN DENTAL PADA ANAK USIA 11-14 TAHUN (STUDI PADA PASIEN YANG MEMILIKI PENGALAMAN DENTAL DI RUMAH SAKIT GIGI MULUT UNSYIAH) (Muhammad Taqwan, 2014) , PERAN MOTIVASI TERHADAP TINGKAT KOOPERATIF PASIEN YANG BERKUNJUNG KE RUMAH SAKIT GIGI DAN MULUT UNSYIAH (Mhd. Parlindungan Berutu, 2017) , |
|
|
Kembali ke halaman sebelumnya
Terkini
PROSPEK EKSPOR KOPI ARABIKA ORGANIK BERSERTIFIKAT DI KABUPATEN ACEH TENGAH |
ANALISIS KOMPARATIF TINGKAT PENDAPATAN USAHATANI PADI SAWAH IRIGASI DAN PADI SAWAH TADAH HUJAN BERDASARKAN STATUS PENGUASAAN LAHAN DI KECAMATAN KUTA COT GLIE KABUPATEN ACEH BESAR |
KAJIAN PEMASARAN DAN KEUNTUNGAN PETANI KACANG TANAH DI KECAMATAN DARUSSALAM KABUPATEN ACEH BESAR |
STUDI PENDAPATAN RUMAH TANGGA PERTANIAN DI DATARAN TINGGI (KASUS DESA URING KECAMATAN BUKIT KABUPATEN BENER MERIAH) |
ANALISIS PENDAPATAN USAHATANI TEMBAKAU DI KECAMATAN BANDAR BARU KABUPATEN PIDIE JAYA |