//
ANALISIS KUAT TARIK DAN ABSORPSI BETON MUTU TINGGI HYBRID MENGGUNAKAN SUBSTITUSI ADITIF PENGGANTI SEMEN, SUBSTITUSI AGREGAT DAN NANOMATERIAL BIJIH BESI (PENGGUNAAN FLY ASH BATU BARA, CANGKANG SAWIT, PASIR POZZOLAN, DAN NANOMATERIAL BIJIH BESI) |
|
![]() |
BACA FULL TEXT ABSTRAK Permintaan Versi cetak |
Pengarang | ADE DWINTA - Personal Name |
---|---|
Abstrak/Catatan ANALISIS KUAT TARIK DAN ABSORPSI BETON MUTU TINGGI HYBRID MENGGUNAKAN SUBSTITUSI ADITIF PENGGANTI SEMEN, SUBSTITUSI AGREGAT DAN NANOMATERIAL BIJIH BESI (Penggunaan Fly Ash Batu Bara, Cangkang Sawit, Pasir Pozzolan, dan Nanomaterial Bijih Besi) Oleh Ade Dwinta NIM. 1509200060037 Komisi Pembimbing 1. Dr. Teuku Budi Aulia, ST., Dipl.Ing 2. Dr. Ir. Muttaqin, MT ABSTRAK Beton mutu tinggi (BMT) didefinisikan sebagai beton yang mempunyai kuat tekan yang disyaratkan lebih besar dari 41,4 MPa (SNI 03-6468-2000). Salah satu kelemahan dari beton mutu tinggi adalah biaya produksi yang mahal. Maka dari itu digunakan material alternatif pengganti berupa limbah pabrik yang ekonomis seperti fly ash batu bara, cangkang sawit, dan pasir pozzolan. Penelitian ini bertujuan untuk mengetahui nilai kuat tarik belah, kuat tarik lentur, dan absorpsi dengan menggunakan material alternatif pengganti sebagai subsitusi aditif, agregat halus, dan agregat kasar serta penambahan filler nanomaterial bijih besi dengan tujuh jenis variasi yang berbeda, yaitu BMT-N, BMT-FBPP, BMT-FBCS, BMT-ASPP, BMT-ASCS, BMT-APPP, dan BMT-APCS. Benda uji untuk pengujian kuat tarik belah berupa silinder berukuran tinggi 30 cm dan diameter 15 cm sebanyak 42 buah, benda uji untuk pengujian kuat tarik lentur berupa balok berukuran 15 cm x 15 cm x 60 cm sebanyak 42 buah, dan benda uji untuk pengujian absorpsi berupa kubus berukuran 5 cm x 5 cm x 5 cm sebanyak 42 buah. Pengujian dilakukan pada umur 28 hari dan 56 hari. Hasil kuat tarik belah maksimum diperoleh pada beton mutu tinggi menggunakan variasi BMT-APPP (abu pozzolan 10%, pasir pozzolan 10%, dan bongkahan cangkang sawit 40%) yaitu dengan hasil kuat tarik belah pada umur 28 hari 5,19 MPa dan pada umur 56 hari dengan nilai 5,58 Mpa. Hasil kuat tarik lentur maksimum diperoleh pada beton mutu tinggi menggunakan variasi BMT-APPP yaitu 5,73 MPa pada umur 28 hari dan 6,11 MPa pada umur 56 hari. Nilai absorpsi beton mutu tinggi normal pada umur 28 hari sebesar 3,89%. Absorpsi beton mutu tinggi normal pada umur 56 hari sebesar 4,63%, lebih besar dari beton mutu tinggi hybrid dengan berbagai variasi. Dari hasil pengujian dapat disimpulkan bahwa BMT-APPP ada variasi terbaik dari penelitian ini. Kata Kunci : Beton mutu tinggi, fly ash batu bara, cangkang sawit, pasir pozzolan, Nanomaterial bijih besi, superplasticizer, kuat tarik belah, kuat tarik lentur, absorpsi. TENSILE STRENGTH AND ABSORPTION ANALYSIS OF HYBRID HIGH QUALITY CONCRETE USING CEMENT REPLACEMENT ADDITIVES SUBSTITUTION, AGGREGATE SUBSTITUTION AND NANOMATERIAL IRON ORE (Use of Coal Fly Ash, Palm Shell, Pozzolan Sand, and Nanomaterial iron ore) By: Ade Dwinta NIM. 1509200060037 Committe of Supervisory: 1. Dr. Teuku Budi Aulia, ST., Dipl.Ing 2. Dr. Ir. Muttaqin, MT ABSTRACT High quality concrete (BMT) is defined as concrete which has a required compressive strength greater than 41.4 MPa (SNI 03-6468-2000). One disadvantage of high quality concrete is the high cost of production. Therefore alternative economical materials such as coal fly ash, palm shells, and pozzolan sand are used as alternative replacement materials. This study aims to determine the value of split tensile strength, flexural tensile strength, and absorption by using alternative substitute materials as substitute additives, fine aggregates, and coarse aggregates and the addition of nanomaterial iron ore fillers with seven different types of variation is BMT-N, BMT-FBPP, BMT-FBCS, BMT-ASPP, BMT-ASCS, BMT-APPP, and BMT-APCS.. The specimens for testing the split tensile strength in the form of cylinders measuring 30 cm high and 15 cm in diameter were 42 pieces, the specimens for testing flexural tensile strength in the form of beams measuring 15 cm x 15 cm x 60 cm were 42 pieces, and the specimens for absorption testing were in the form of 42 cubes in size of 5 cm x 5 cm x 5 cm. The tests were carried out at 28 days and 56 days. The results showed that high quality concrete using variations of BMT-APPP (10% of pozzolan ash, 10 % of pozzolan sand, and 40% palm shell) with the result of split tensile strength at 28 days is 5.19 MPa and at the age of 56 days with a value of 5.58 MPa. Maximum tensile flexural strength results obtained in high quality concrete using BMT-APPP variations, namely the results of flexural tensile strength at 28 days 5.73 MPa and at the age of 56 days with a value of 6.11 MPa. Absorption value of high quality normal concrete at 28 days is 3.89%. Absorption of normal high quality concrete at 56 days is 4.63%, greater than hybrid high quality concrete with various variations. From the test results it can be concluded that BMT-APPP is the best variation of this study. Keywords : High quality concrete, coal fly ash, palm shell, pozzolan sand, nanomaterial iron ore, superplasticizer, split tensile strength, flexural tensile strength, absorption. | |
Tempat Terbit | |
Literature Searching Service | Hard copy atau foto copy dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan isi formulir online (Chat Service LSS) |
Share Social Media | |
Tulisan yang Relevan PENGARUH SUBSTITUSI SEMEN, AGREGAT HALUS, DAN AGREGAT KASAR TERHADAP KUAT TEKAN DAN KUAT GESER MURNI BETON MUTU TINGGI. (PENGGUNAAN FLY ASH BATU BARA, CANGKANG SAWIT, PASIR POZZOLAN DAN NANOMATERIAL BIJIH BESI). (NORA USRINA, 2017) |
|
Kembali ke sebelumnya |