Abstrak

Baca Juga : ANALISIS KUAT TEKAN DAN KUAT TARIK BELAH BETON MUTU ULTRA TINGGI MENGGUNAKAN FLY ASH BATU BARA SEBAGAI ADITIF DAN BIJIH BESI SEBAGAI FILLER YANG DITAMBAHKAN SERAT POLYPROPYLENE (Edi Mardiono, 2020) ,

Baca Juga : PENGARUH SUBSTITUSI SEMEN, AGREGAT HALUS, DAN AGREGAT KASAR TERHADAP KUAT TEKAN DAN KUAT GESER MURNI BETON MUTU TINGGI. (PENGGUNAAN FLY ASH BATU BARA, CANGKANG SAWIT, PASIR POZZOLAN DAN NANOMATERIAL BIJIH BESI). (NORA USRINA, 2017) ,

rat semen, fas yang digunakan adalah 0,2 dengan penambahan superplasticizer sebanyak 1,5% dari berat semen dengan target kuat tekan menjadi lebih dari 130 mpa. benda uji untuk kuat tekan beton berupa silinder berukuran 10 cm × 20 cm sebanyak 18 benda uji. pengujian kuat tekan beton dilakukan pada umur beton 7, 28, dan 56 hari. nilai kuat tekan beton normal pada umur 7, 28, dan 56 hari sebesar 92,44 mpa, 125,53 mpa, dan 130,42 mpa. kuat tekan beton dengan penambahan 15% fly ash sebesar 94,42 mpa, 128,86 mpa, dan 133,37 mpa. klasifikasi mutu pekerjaan tergolong sedang sampai sangat baik. perhitungan analisa varian menghasilkan f0 hitung > f0 tabel menunjukkan bahwa penambahan fly ash batu bara dan umur beton mempengaruhi kekuatan mekanis beton. kata kunci : beton mutu ultra tinggi, fly ash batubara, bijih besi, kuat tekan abstract development in infrastructure decades has progressed very rapidly due to geometric demands and construction methods, more buildings, bridges and so on that use quality concrete and very high performance. high quality concrete is a high-performance concrete type that generally has a strong press of 40 mpa or more. but now, concrete is said to be a very high quality concrete if the power is above 80 mpa, while 120 mpa can be categorized as ultra-high quality concrete (mulyono,2005). this research aims to increase the quality of concrete higher and know the comparison of the mixture in ultra high quality concrete that uses additives with ultra high quality concrete without the use of additives against the mechanical properties of concrete. this study used a variation of test objects using coal fly ash substitution as much as 15% and 0% of the volume of cement, iron ore used as 6% filler from the weight of cement, the fas used is 0.2 with the addition of solid as much as 1.5% from the weight of cement with a strong target press to more than 130 mpa. the test material for solid concrete press is a cylinder measuring 10 cm × 20 cm as many as 18 test objects. strong concrete press testing is done at concrete age 7, 28, and 56 days. the normal strong concrete press value is at 7, 28, and 56 days at 92.44 mpa, 125.53 mpa, and 130.42 mpa. strong concrete press with 15% addition of fly ash for 94.42 mpa, 128.86 mpa, and 133.37 mpa. classification of work quality is medium to very good. calculation of variant analysis resulted in f0 count > f0 the table showed that the addition of coal fly ash and the age of concrete affects the mechanical strength of concrete. keywords: ultra high quality concrete, coal fly ash, iron ore, compressive

Tulisan yang relevan

ANALISIS KUAT TARIK BELAH BETON MUTU ULTRA TINGGI MENGGUNAKAN FLY ASH BATU BARA SEBAGAI ADITIF DAN NANO BIJIH BESI SEBAGAI FILLER (FIRDHA RIANSYAH, 2020) ,

ANALISIS KUAT TARIK LENTUR BETON MUTU ULTRA TINGGI MENGGUNAKAN FLY ASH BATU BARA SEBAGAI ADITIF DAN NANO BIJIH BESI SEBAGAI FILLER GAI FILLER (SAID HOFFIF HIDAYAT ALATAS, 2020) ,

KUAT TEKAN BETON MUTU ULTRA TINGGI 130 MPA MENGGUNAKAN FLY ASH BATU BARA SEBAGAI ADITIF DAN BIJIH BESI SEBAGAI FILLER (M.ARIF FAYADH, 2020) ,