ANGGUN S W A. PEMBUATAN KOMPOSIT KITOSAN MAGNETIK TERSULFONASI BERIKATAN SILANG GLUTARALDEHID SEBAGAI ADSORBEN MERKURI. Banda Aceh : Fakultas MIPA Universitas Syiah Kuala, 2019 |
|
Abstrak
abstrak
pembuatan komposit kitosan magnetik tersulfonasi berikatan silang glutaraldehid (k-bm-s-gla) telah berhasil dilakukan dan diaplikasikan sebagai adsorben merkuri. pembuatan komposit k-bm-s-gla dilakukan dengan variasi komposisi kitosan tersulfonasi, pasir besi dan glutaraldehid (gla). pasir besi diperoleh dari pantai syiah kuala, banda aceh. komposit k-bm-s-gla dikarakterisasi menggunakan fourier transform infrared (ft-ir), x-ray diffraction (xrd) dan scanning electron microscope (sem). komposisi terbaik dari komposit k-bm-s-gla yaitu 0,65 g kitosan tersulfonasi, 0,5 g pasir besi dan gla 0,17 m. hasil uji adsorpsi menunjukkan bahwa kapasitas adsorpsi tertinggi diperoleh pada waktu kontak 60 menit dan ph 3. adsorpsi merkuri menggunakan komposit k-bm-s-gla mengikuti model isoterm adsorpsi langmuir dan freundlich. kapasitas adsorpsi maksimum berdasarkan isoterm adsorpsi langmuir adalah 93,46 mg/g. aplikasi adsorben pada limbah pertambangan emas menunjukkan persen penghilangan
Baca Juga : PEMBUATAN KOMPOSIT KITOSAN MAGNETIK TERSULFONASI BERIKATAN SILANG GLUTARALDEHID SEBAGAI ADSORBEN MERKURI (ANGGUN S W A, 2019) ,
Baca Juga : MODIFIKASI KITOSAN MENGGUNAKAN PASIR BESI, PENGIKAT SILANG PEGDE DAN HIDROLISAT PROTEIN DARI BIJI PETAI CINA SEBAGAI ADSORBEN ION LOGAM KADMIUM (CUT PUTRI AULIA, 2020) , erkuri mencapai 98,24%. kata kunci: glutaraldehid, kitosan, merkuri, pasir besi, sulfonasi abstract preparation of glutaraldehyde crosslinked sulfonated magnetic chitosan composite (k-bm-s-gla) has been successfully conducted and applied as an adsorbent of mercury. k-bm-s-gla composites were prepared with various composition of sulfonated chitosan, iron sand, and glutaraldehyde (gla). iron sand was obtained from syiah kuala beach, banda aceh. k-bm-s-gla composites were characterized using fourier transform infrared (ft-ir), x-ray diffraction (xrd) and scanning electron microscope (sem). the best composition of k-bm-s-gla composites was 0.65 g sulfonated chitosan, 0.5 g iron sand and gla 0.17 m. based on adsorption study, the highest adsorption capacity was obtained at the contact time of 60 minutes and ph 3. mercury adsorption by the k-bm-s-gla composites fitted to both langmuir and freundlich adsorption isotherm models. the maximum adsorption capacity based on langmuir's adsorption isotherm was 93.46 mg/g. the application of adsorbent in the gold mining waste showed the percentage of mercury removal was reached 98.24%. keywords: chitosan, glutaraldehyde, iron sand, mercury, Tulisan yang relevan MODIFIKASI KITOSAN MENGGUNAKAN PASIR BESI DAN GLUTARALDEHID SERTA APLIKASINYA SEBAGAI ADSORBEN LIMBAH MERKURI DI PERTAMBANGAN EMAS MANGGAMAT, ACEH (FITRI PURNAMA WATI, 2018) ,PEMBUATAN DAN KARAKTERISASI KOMPOSIT KITOSAN MAGNETIK BERIKATAN SILANG H2SO4 DAN APLIKASINYA SEBAGAI ADSORBEN METHYLENE BLUE (ISHMATURRAHMI, 2018) , UJI DAYA SERAP LOGAM CD (II) MENGGUNAKAN KOMPOSIT KRISTOBALIT-KHITOSAN BERIKATAN SILANG (Irwansyah, 2015) , |
|
|
|
Kembali ke halaman sebelumnya
Terkini
PROSPEK EKSPOR KOPI ARABIKA ORGANIK BERSERTIFIKAT DI KABUPATEN ACEH TENGAH |
ANALISIS KOMPARATIF TINGKAT PENDAPATAN USAHATANI PADI SAWAH IRIGASI DAN PADI SAWAH TADAH HUJAN BERDASARKAN STATUS PENGUASAAN LAHAN DI KECAMATAN KUTA COT GLIE KABUPATEN ACEH BESAR |
KAJIAN PEMASARAN DAN KEUNTUNGAN PETANI KACANG TANAH DI KECAMATAN DARUSSALAM KABUPATEN ACEH BESAR |
STUDI PENDAPATAN RUMAH TANGGA PERTANIAN DI DATARAN TINGGI (KASUS DESA URING KECAMATAN BUKIT KABUPATEN BENER MERIAH) |
ANALISIS PENDAPATAN USAHATANI TEMBAKAU DI KECAMATAN BANDAR BARU KABUPATEN PIDIE JAYA |