DHEYA AMELIA GINTING`S. PENGARUH PENAMBAHAN 5% SILIKA NANOPARTIKEL DARI PASIR LAUT PADA GLASS IONOMER CEMENT TIPE II TERHADAP TINGKAT KEBOCORAN MIKRO. Banda Aceh : Fakultas Kedokteran Gigi Universitas Syiah Kuala, 2019 |
|
AbstrakAbstrak
nama : dheya amelia ginting
program studi : pendidikan dokter gigi
fakultas : kedokteran gigi
judul : pengaruh penambahan 5% silika nano partikel dari pasir laut pada glass ionomer cement tipe ii terhadap tingkat kebocoran mikro
masalah yang sering timbul pada restorasi gigi adalah terjadinya kebocoran mikro pada tepi restorasi. penyebab utama kebocoran mikro adalah material restorasi yang gagal beradaptasi dengan struktur gigi sehingga menyebabkan terbentuknya celah diantara keduanya, kondisi tersebut memungkinkan masuknya cairan mulut ke dalam celah tersebut. ikatan kimia yang lebih kuat antara gic dan gigi dapat dicapai dengan mencampurkan gic dengan bahan bioaktif yaitu silika untuk membentuk hidroksiapatit pada permukaan gic yang diharapkan mampu mengurangi terbentuknya celah marginal. penelitian ini bertujuan untuk mendapatkan informasi tentang pengaruh penambahan silika pada gic terhadap tingkat kebocoran mikro. spesimen penelitian berjumlah 20 gigi
Baca Juga : KEKERASAN PERMUKAAN GLASS IONOMER CEMENT (GIC) SETELAH PENAMBAHAN 5% SILIKA DARI PASIR LAUT (Apriliadi Saputra, 2018) ,
Baca Juga : GAMBARAN KETEBALAN BIOFILM PADA GLASS IONOMER CEMENT (GIC) TIPE II MODIFIKASI PENAMBAHAN SILIKA DARI SINTESIS PASIR PANTAI (REZA UMAMI, 2019) , lar rahang atas dengan mahkota yang masih baik dan tidak ada karies dan dibagi menjadi dua kelompok. kelompok a menggunakan gic tipe ii dan kelompok b gic tipe ii yang ditambahkan silika nanopartikel. spesimen diaplikasikan bahan restorasi dan di rendam dalam larutan methylene blue selama 24 jam. spesimen diamati dengan stereomikroskop dan di ukur tingkat kebocorannya. skor kebocoran mikro menggunakan metode penetrasi dye dengan 5 skor yaitu skor 0,1,2,3 dan 4. data dianalisis dengan menggunakan statistik non-parametrik (uji mann whitney) menunjukkan bahwa tidak terdapat pengaruh yang signifikan pada skor kebocoran mikro antara kelompok a dan b (p>0,05). kata kunci : kebocoran mikro, glass ionomer cement, silika , hidroksiapatit abstract name : dheya amelia ginting study program : dentistry faculty : dentistry title : effect of adding 5% silica nano particles from sea sand on glass ionomer cement type ii to microleakage levels the problem that often arises in tooth restoration is the occurrence of microleakge on the edges of the restoration. the main cause of microleakage is a restoration material that fails to adapt to the tooth structure causing a gap between the two, allowing the entry of oral fluid into the gap. the stronger chemical bond between gic and teeth can be achieved by mixing gic with bioactive ingredients, namely silica to form hydroxyapatite at the gic surface which is expected to reduce the formation of marginal slits. this study aims to obtain information about the effect of adding silica to gic on microleakage rates. the study specimens were 20 maxillary premolars with crowns that were still good and had no caries and were divided into two groups. group a uses gic type ii and group b gic type ii which are added by silica nanoparticles. specimens were applied to the restoration material and soaked in methylene blue solution for 24 hours. specimens were observed with stereomycroscopes and measured the level of leakage. the micro leakage score used the dye penetration method with 5 scores namely scores of 0,1,2,3 and 4. data analyzed using non-parametric statistics (mann whitney test) showed that there was no significant effect on the micro leakage score between group a and b (p> 0.05). keyword : microleakage, glass ionomer cement, silica, Tulisan yang relevan ANALISIS HASIL MODIFIKASI GLASS IONOMER CEMENT DENGAN PENAMBAHAN HIDROKSIAPATIT DAN SILIKA DARI BAHAN ALAM (DITINJAU DARI GUGUS FUNGSI MENGGUNAKAN FOURIER TRANSFORM INFRARED) (MOHD TAUFIQ KAMIL H, 2018) ,GAMBARAN PERLEKATAN GLASS IONOMER CEMENT MODIFIKASI SILIKA 5% DARI PASIR LAUT DENGAN GIGI MENGGUNAKAN SCANNING ELECTRON MICROSCOPE (SEM) (DWI SEPTIANI, 2019) , PENGARUH PENAMBAHAN SILIKA 5% DARI PASIR LAUT TERHADAP PERUBAHAN DIMENSI GLASS IONOMER CEMENT SETELAH PERENDAMAN KOPI ARABIKA GAYO (Halisni, 2019) , |
|
|
Kembali ke halaman sebelumnya
Terkini
PROSPEK EKSPOR KOPI ARABIKA ORGANIK BERSERTIFIKAT DI KABUPATEN ACEH TENGAH |
ANALISIS KOMPARATIF TINGKAT PENDAPATAN USAHATANI PADI SAWAH IRIGASI DAN PADI SAWAH TADAH HUJAN BERDASARKAN STATUS PENGUASAAN LAHAN DI KECAMATAN KUTA COT GLIE KABUPATEN ACEH BESAR |
KAJIAN PEMASARAN DAN KEUNTUNGAN PETANI KACANG TANAH DI KECAMATAN DARUSSALAM KABUPATEN ACEH BESAR |
STUDI PENDAPATAN RUMAH TANGGA PERTANIAN DI DATARAN TINGGI (KASUS DESA URING KECAMATAN BUKIT KABUPATEN BENER MERIAH) |
ANALISIS PENDAPATAN USAHATANI TEMBAKAU DI KECAMATAN BANDAR BARU KABUPATEN PIDIE JAYA |