Rani Milda Yanti. GAMBARAN KETEBALAN BIOFILM PADA GLASS IONOMER CEMENT MODIFIKASI HIDROKSIAPATIT 5% DARI SINTESIS CANGKANG KERANG DARAH (ANADARA GRANOSA). Banda Aceh : Universitas Syiah Kuala, 2019 |
|
AbstrakAbstrak
nama : rani milda yanti
fakultas : kedokteran gigi
program studi : pendidikan dokter gigi
judul : gambaran ketebalan biofilm pada glass ionomer cement
modifikasi hidroksiapatit 5% dari sintesis cangkang
kerang darah (anadara granosa)
biofilm adalah koloni bakteri terstruktur yang melekat pada permukaan substrat contohnya pada restorasi glass ionomer cement (gic) di rongga mulut. gic mengandung fluor sebagai antibakteri untuk menghambat akumulasi bakteri, namun gic masih memiliki kekurangan yaitu porus pada permukaannya. ketebalan biofilm terbentuk tergantung banyak koloni bakteri yang melekat pada permukaan. hidroksiapatit yang disintesis dari cangkang kerang darah (anadara granosa) dapat ditambahkan pada gic. penelitian ini bertujuan untuk melihat ketebalan biofilm yang terbentuk pada gic modifikasi penambahan hidroksiapatit. spesimen berjumlah 12 buah dikelompokkan menjadi 2 kelompok yaitu gic tipe ii tanpa dan dengan penambahan hidroksiapatit dan
Baca Juga : KEKERASAN PERMUKAAN GLASS IONOMER CEMENT SETELAH PENAMBAHAN 5% HIDROKSIAPATIT DARI CANGKANG KERANG DARAH (ANADARA GRANOSA) (FIKRIYADI NURZAL, 2018) ,
Baca Juga : GAMBARAN KETEBALAN BIOFILM PADA GLASS IONOMER CEMENT MODIFIKASI HIDROKSIAPATIT 5% DARI SINTESIS CANGKANG KERANG DARAH (ANADARA GRANOSA) (Rani Milda Yanti, 2019) , direndam dalam media yang berisi biofilm selama 24 jam, 48 jam dan 72 jam yang berasal dari hasil swab gigi molar volunteer yang ditumbuhkan pada media brain heart infusin broth (bhib) dan dilakukan pengujian dengan alat scanning electron microscopy (sem). ketebalan biofilm yang terbentuk pada permukaan spesimen diamati dalam bentuk gambar dan tabel. hasil penelitian menunjukkan rata-rata ketebalan biofilm pada gic tipe ii tanpa penambahan hidroksiapatit pada waktu 24 jam, 48 jam dan 72 jam secara berurutan adalah 0 µm, 28.95 µm, 76.2 µm. sedangkan pada gic tipe ii dengan penambahan hidroksiapatit adalah 0 µm, 4.05 µm, 14.2 µm. kesimpulan penelitian ini adalah ketebalan biofilm pada gic tipe ii tanpa penambahan hidroksiapatit lebih tebal dibandingkan dengan yang ditambahkan hidroksiapatit. kata kunci : ketebalan biofilm, glass ionomer cement (gic), hidroksiapatit, scanning electron microscopy (sem). abstract name : rani milda yanti faculty : dentistry study program : dentistry title : description of biofilm thickness on glass ionomener cement modified by 5% hydroxyapatite synthesis of blood clam shells (anadara granosa) biofilms are structured bacterial colonies that attach to the surface of the substrate, for example in glass ionomer cement (gic) restorations in the oral cavity. gic contains fluorine as an antibacterial to inhibit bacterial accumulation, but gic still has the disadvantage of being porous on its surface. the thickness of the biofilm is formed depending on many bacterial colonies that are attached to the surface. hydroxyapatite synthesized from blood clams (anadara granosa) can be added to gic. this study aims to observe the thickness of the biofilm formed in the gic modification of the addition of hydroxyapatite. 12 specimens were grouped into 2 groups, namely gic type ii without and with the addition of hydroxyapatite and soaked in media containing biofilms for 24 hours, 48 hours and 72 hours derived from the results of voluntary molar tooth swabs grown on brain heart infusin broth media (bhib) and tested by scanning electron microscopy (sem). biofilm thickness formed on the surface of the specimen was observed in the form of images and tables. the results showed that the average biofilm thickness in gic type ii without the addition of hydroxyapatite at 24 hours, 48 hours and 72 hours respectively was 0 µm, 28.95 µm, 76.2 µm. whereas in gic type ii with the addition of hydroxyapatite is 0 µm, 4.05 µm, 14.2 µm. conclusion of this study was the thickness of the biofilm in gic type ii without the addition of hydroxyapatite was thicker than that added with hydroxyapatite. keywords : biofilm thickness, glass ionomer cement (gic), hydroxyapatite, scanning electron microscopy Tulisan yang relevan ANALISIS HASIL MODIFIKASI GLASS IONOMER CEMENT DENGAN PENAMBAHAN HIDROKSIAPATIT DAN SILIKA DARI BAHAN ALAM (DITINJAU DARI GUGUS FUNGSI MENGGUNAKAN FOURIER TRANSFORM INFRARED) (MOHD TAUFIQ KAMIL H, 2018) ,GAMBARAN KETEBALAN BIOFILM PADA KOMBINASI GIC TIPE II DENGAN HAP DARI CANGKANG KERANG DARAH (ANADARA GRANOSA) DAN SIO2 DARI PASIR LAUT MENGGUNAKAN SCANNING ELECTRON MICROSCOPY (SEM) (AULIYA ATTAMIMI, 2019) , GAMBARAN PENGGUNAAN BAHAN AMALGAM, RESIN KOMPOSIT DAN GLASS IONOMER CEMENT (GIC) DI RUMAH SAKIT GIGI DAN MULUT UNSYIAH PADA BULAN JULI – DESEMBER 2014 (Nur Shabrina, 2016) , |
|
|
Kembali ke halaman sebelumnya
Terkini
PROSPEK EKSPOR KOPI ARABIKA ORGANIK BERSERTIFIKAT DI KABUPATEN ACEH TENGAH |
ANALISIS KOMPARATIF TINGKAT PENDAPATAN USAHATANI PADI SAWAH IRIGASI DAN PADI SAWAH TADAH HUJAN BERDASARKAN STATUS PENGUASAAN LAHAN DI KECAMATAN KUTA COT GLIE KABUPATEN ACEH BESAR |
KAJIAN PEMASARAN DAN KEUNTUNGAN PETANI KACANG TANAH DI KECAMATAN DARUSSALAM KABUPATEN ACEH BESAR |
STUDI PENDAPATAN RUMAH TANGGA PERTANIAN DI DATARAN TINGGI (KASUS DESA URING KECAMATAN BUKIT KABUPATEN BENER MERIAH) |
ANALISIS PENDAPATAN USAHATANI TEMBAKAU DI KECAMATAN BANDAR BARU KABUPATEN PIDIE JAYA |