Firdaus. PENURUNAN WARNA METHYLENE BLUEDALAM AIRRNMENGGUNAKAN FOTOKATALISRNLA-DOPED NATAO3. Banda Aceh : Fakultas Pasca Sarjana Universitas Syiah Kuala, 2015 |
|
AbstrakAbstrak
fotokatalis la-doped natao
3
.telah disintesis dengan mengunakan mitode sol dan
gel pada temperatur 800
o
c. penelitian ini bertujuan mendegradasi limbah zat warna
(methlyene blue) dalam air dengan mengunakan mitode fotokatalisis,katalis
dikarateristik dengan mengunakan x-ray defractofometer (xrd), dan scaning
electron microscopy (sem).hasil dari pada analisa (sem) terlihat struktur dan
bentuk dari partikel, dan hasil dari spectrum (xrd) menunjukan derajat kristalisasi
yang tinggi.persentase degradasi methlyene blue semakin meningkat dengan
bertambahnya nilai ph. analisa sampel larutan methlyene blue dilakukan dengan
spectrofotometer untuk mengetahui penurunan methyleneblue secara
fotokatalisis.persen degradasi terbesar terlihat pada ph 9, mencapai angka 87 %.
semakin lama waktu radiasi maka persen degradasi methlyene blue semakin
meningkat. hal ini disebabkan radikal hidroksil yang dihasilkan semakin banyak.
demikian juga penambahan h2o2
dan
Baca Juga : PENURUNAN WARNA METHYLENE BLUEDALAM AIRRNMENGGUNAKAN FOTOKATALISRNLA-DOPED NATAO3 (Firdaus, 2015) ,
Baca Juga : PENGARUH SUHU AKTIVASI CANGKANG TELUR TERHADAP DAYA SERAP METILEN BIRU (Deny Anggraini, 2016) , aoh dalam larutan methlyene blue menghasilkan peningkatan degradasi yang signifikan mencapai 88%. kata kunci : methylen blue, la-doped natao 3, fotokatalisis. ix abstract photo catalyst la-dope natao3, has been synthetized using sol method and gel on the temperature of 800oc. the purpose of this study is to break down the dye effluent (methylene blue) in the water by using photo catalyst method, where catalyst is characterized by using x-ray defractofometer (xrd), and scanning electron microscopy (sem). the results were taken from the analyzed data by using sem shown that the structure and the form of the particles, and the xrd results were also in the high crystallization. the percentage of methylene blue degradation was getting higher as the increasing of ph value. the analyzed sample of methylene blue was executed by using spectrophotometer in order to know the reduction of methylene blue analytically. the biggest analysis percentage on the ph of 9, was getting 87 in percentage. the longer radiation time used the higher methylene blue obtained. it was because of the radical hydroxyl was obtained higher, and also the addition of h2o2 and naoh in methylene blue resulted the increment of significant degradation until 88%. key words: methylene blue, la doped natao3, photo Tulisan yang relevan PRODUKSI GREEN HIDROGEN DARI H2O SEBAGAI BAHAN BAKAR ALTERNATIF MELALUI PROSES FOTOKATALISIS DENGAN MENGGUNAKAN LA-DOPED NATAO3 (saisa, 2014) ,UJI DAYA SERAP METILEN BIRU MENGGUNAKAN KARBON AKTIF DARI LIMBAH CANGKANG MELINJO YANG DIMODIFIKASI DENGAN LIMBAH CANGKANG TELUR (Farhan Fuad, 2019) , DEGRADASI ZAT WARNA KATIONIK DAN ANIONIK MENGGUNAKAN IMMOBILISASI FOTOKATALIS TIO2/?-FE2O3/BENTONIT DIBAWAH LAMPU FLUORESCENCE (FERIZKA FRASTIWI, 2018) , |
|
|
|
Kembali ke halaman sebelumnya
Terkini
PROSPEK EKSPOR KOPI ARABIKA ORGANIK BERSERTIFIKAT DI KABUPATEN ACEH TENGAH |
ANALISIS KOMPARATIF TINGKAT PENDAPATAN USAHATANI PADI SAWAH IRIGASI DAN PADI SAWAH TADAH HUJAN BERDASARKAN STATUS PENGUASAAN LAHAN DI KECAMATAN KUTA COT GLIE KABUPATEN ACEH BESAR |
KAJIAN PEMASARAN DAN KEUNTUNGAN PETANI KACANG TANAH DI KECAMATAN DARUSSALAM KABUPATEN ACEH BESAR |
STUDI PENDAPATAN RUMAH TANGGA PERTANIAN DI DATARAN TINGGI (KASUS DESA URING KECAMATAN BUKIT KABUPATEN BENER MERIAH) |
ANALISIS PENDAPATAN USAHATANI TEMBAKAU DI KECAMATAN BANDAR BARU KABUPATEN PIDIE JAYA |